UV CURABLE RESIN

The Uses of UV CURABLE RESIN

• Cures rapidly to form a glassy, high modulus, and optically clear material.
• Excellent for use in protective coatings, optical, and outdoor applications.
• Non-yellowing.
• Low oxygen inhibition.
• Mechanical properties after curing:

Modulus*: 1140 MPa
Strength*: 35 MPa
Elongation*: 5%
Pencil Hardness: 6H
Tack Free**: 15

*Test resources: Tensile tester, 35 mm gauge length, 1.0 mm thickness, 6.5 mm width.
** Cured under stated intensity. Medium pressure mercury bulb with 320-500 nm filter. Adhesion tests were conducted using a cross hatch tape test on films 0.125 mm thick on glass and PET. Material Data using ASTM D 638-02a.

The Uses of UV CURABLE RESIN

• Cures extremely rapidly to form a glassy, high modulus material.
• Excellent for use in optical applications.
• High refractive index - 1.54.
• High impact absorption.
• Non-yellowing.
• No oxygen inhibition.
• Mechanical properties after curing:

Modulus*: 208 MPa
Strength*: 7 MPa
Elongation*: 54%
Pencil Hardness: 6H
Tack Free**: 3 min

*Test resources: Tensile tester, 35 mm gauge length, 1.0 mm thickness, 6.5 mm width.
** Cured under stated intensity. Medium pressure mercury bulb with 320-500 nm filter. Adhesion tests were conducted using a cross hatch tape test on films 0.125 mm thick on glass and PET. Material Data using ASTM D 638-02a.

General Description

Storage:

• The storage temperature should not exceed 35 °C.
• Keep tightly closed. Store in a cool, dry, well-ventilated area.
• Do not expose to ultraviolet light.
• High temperatures (>80 °C), pressure, and contamination with peroxides may result in auto-polymerization of the product.
• Unstable upon depletion of inhibitor.